Engineering SLA Series - Heavy Duty Resin is a SLA 3D printing resin that features an unsurpassed combination of impressive flexural strength with high-temperature resistance and durability.

€ 78,50 78.5 EUR € 78,50

€ 78,50

Not Available For Sale


  • Color
  • Weight
  • Weight

This combination does not exist.


Name :
[ERSLAHD-NTRL-00500] Engineering SLA Resin - Heavy Duty
SKU :
ERSLAHD-NTRL-00500
EAN :
8719956553097

The Engineering SLA Resin – Heavy Duty is one of the strongest resins on the market. It combines flexural strength with durability and heat resistance. Parts printed with this resin show great resistance to continuous built-up pressure. This resin is perfectly suitable for applications that need strength, stiffness and heat resistance.

Key features

  • Flexural strength of 135 MPa
  • Stiff and durable
  • High heat resistance of 128°C
  • High dimensional accuracy and low shrinkage
  • Almost odorless processing
  • Compatible with all open-source SLA, DLP, and LCD 3D printers in the range of 385 – 405nm

 

Applications

  • Tooling
  • Jigs and fixtures
  • Manufacturing aids
  • Mold masters for low volume injection molding
  • Functional prototyping

Resin properties (uncured liquid)

  • Viscosity: 550 cps at 25°C
  • Density: 1.12 g/cm2

 

Print Settings:

Anycubic Mono X

50µm

First / Burn-in / Bottom Layers: 2x to 4x for 55 to 60 Seconds

Exposure Time Normal Layers: 4 to 5 Seconds

Lifting Distance: 6mm

Bottom Lifting Distance: 8mm

Lifting Speed:85mm/min & 240mm/min

Rest Time Before Lift: 2 Seconds

UV Power: 100%

Mechanical properties

Test method on post cured objects through 10 minutes high power mercury curing.

PropertiesTypical ValueTest Method
Glass transition temperature (Tg)128°CASTM D7028
Water absorption0.45%ASTM D570-98
Impact strength (IZOD notched)20 J/mASTM D256A
Tensile strength91 MPaASTM D638M
Tensile Modulus2500 MPaASTM D638M
Elongation at break8%ASTM D638M
Flexural Strength135 MPaASTM D790M
Flexural Modulus3250 MPaASTM D2240
Shore D Hardness87ASTM D2240

Please note that the above-displayed values can vary with individual machine processing, post-curing parts,  geometry, print orientation, print settings, and temperature.

 

Preparation(s) before starting to print

  • Shake the bottle for at least 2 minutes before each use
  • After shaking the bottle, leave the resin to rest for 10 minutes to let air bubbles get out of the resin
  • The resin can be poured back from the vat into the bottle once your print is finished
  • Always use protective measurements like safety glasses and nitrile gloves when handling resins

 

Post-processing

We do advise you to post-process your 3D print in order to achieve the material properties.

  • Rinse your 3D printed object in IPA or (Bio)Ethanol for approximately 5 minutes
  • An ultrasonic cleaner is preferred/recommended
  • Make sure that IPA and/or (Bio)Ethanol rinsed objects are perfectly dry before further post-curing.
  • Place the rinsed parts in a well-ventilated area for at least 30 minutes, or use pressurized air for at least 2 minutes
  • Cure your object in a high power curing chamber for approximately 20-30 minutes at 65° C
  • The preferred curing wavelength is between 300-410nm

 

Safety

Please always be aware that when 3D printing with resins that you are working with chemicals and that you should always be cautious and use the personal protective equipment as stipulated in our safety data sheets.

  • Always wear Respiratory Protection when sanding/cutting the resin object
  • Always use nitrile gloves when handling resins and uncured resin objects

 

Product export information

HS Code: 2916140090Description: Resin for 3D PrintingCountry of origin: the Netherlands

formfutura-sds-engineeringslaheavydutyresin.pdf
Download
formfutura-tds-engineeringslaheavyduty.pdf
Download