Engineering SLA Series - Heavy Duty Resin
Flexural strength of 135 MPa
Stiff and durable
High heat resistance of 128°C
High dimensional accuracy and low shrinkage
Almost odorless processing
Compatible with all open-source SLA, DLP, and LCD 3D printers in the range of 385 - 405nm
Jigs and fixtures
Mold masters for low volume injection molding
Resin properties (uncured liquid)
Viscosity: 550 cps at 25°C
Density: 1.12 g/cm2
Test method on post cured objects through 10 minutes high power mercury curing.
Glass transition temperature (Tg)
Impact strength (IZOD notched)
Elongation at break
Shore D Hardness
Please note that the above-displayed values can vary with individual machine processing, post-curing parts, geometry, print orientation, print settings, and temperature.
Preparation(s) before starting to print
Shake the bottle for at least 2 minutes before each use
After shaking the bottle, leave the resin to rest for 10 minutes to let air bubbles get out of the resin
The resin can be poured back from the vat into the bottle once your print is finished
Always use protective measurements like safety glasses and nitrile gloves when handling resins
We do advise you to post-process your 3D print in order to achieve the material properties.
Rinse your 3D printed object in IPA or (Bio)Ethanol for approximately 5 minutes
An ultrasonic cleaner is preferred/recommended
Make sure that IPA and/or (Bio)Ethanol rinsed objects are perfectly dry before further post-curing.
Place the rinsed parts in a well-ventilated area for at least 30 minutes, or use pressurized air for at least 2 minutes
Cure your object in a high power curing chamber for approximately 20-30 minutes at 65° C
The preferred curing wavelength is between 300-410nm
Please always be aware that when 3D printing with resins that you are working with chemicals and that you should always be cautious and use the personal protective equipment as stipulated in our safety data sheets.
Always wear Respiratory Protection when sanding/cutting the resin object
Always use nitrile gloves when handling resins and uncured resin objects
Product export information
|HS Code: 2916140090||Description: Resin for 3D Printing||Country of origin: the Netherlands|
Specifications for Engineering SLA Series - Heavy Duty Resin